0.88C-1.2Si-0.75Mn-2Al高强度电缆铠装钢用盘条的试制

采用中高碳成分添加低密度元素Si、Al进行轻量化的设计思路设计了试验钢的化学成分,试验钢采用50 kg真空感应炉冶炼。利用金相显微镜、SEM扫描电镜和力学性能检测设备对试制后的Φ6 mm盘条进行了显微组织观察、珠光体片层间距的测量和屈服强度、抗拉强度、延伸率的检验。结果表明:盘条在600℃等温2 h后的金相显微组织为铁素体+珠光体的混合组织,珠光体的片层间距为(126±5) nm,屈服强度大于1 183 MPa、抗拉强度大于1 425 MPa、延伸率大于10%,其力学性能满足电缆用铠装钢的技术要求。     

中国移动通信电源专辑序

通信电源是保障整个通信网络正常运行的关键基础设施,安全和节能是通信电源专业永恒的主题,根据年度工作计划安排,中国移动通信集团公司网络部在2006年初开展了通信电源专辑论文征集活动,该活动共收到26个省上报的155篇论文,经集团公司、北京、广东、浙江、江苏、江西省公司和京移通信设计院编辑部组成的评审委员会专家们的认真评选,共评选出一等奖7篇,二等奖8篇,三等奖12篇.     

Fenton氧化法去除酱油生产废水中焦糖色素的研究

着重考察了Fenton试剂对水中焦糖色素降解的影响因素.从试验中得出,这些影响因素包括pH、催化剂的投加方式、催化剂与氧化剂的化学计量数以及反应时间等.Fenton反应中,pH4的条件下处理效果最好,反应进行40min时去除率达到90%.     

The effect of grain size, strain rate, and temperature on the mechanical behavior of commercial purity aluminum

Commercial purity aluminum AA1050 was subjected to equal channel angular extrusion (ECAE) that resulted in an ultrafine-grained (UFG) microstructure with an as-received grain size of 0.35 μm. This UFG material was then annealed to obtain microstructures with grain sizes ranging from 0.47 to 20 μm. Specimens were compressed at quasi-static, intermediate, and dynamic strain rates at temperatures of 77 and 298 K. The mechanical properties were found to vary significantly with grain size, strain rate, and temperature. Yield stress was found to increase with decreasing grain size, decreasing temperature, and increasing strain rate. The work hardening rate was seen to increase with increasing grain size, decreasing temperature, and increasing strain rate. The influence of strain rate and temperature is most significant in the smallest grain size specimens. The rate of work hardening is also influenced by strain rate, temperature, and grain size with negative rates of work hardening observed at 298 K and quasi-static strain rates in the smallest grain sizes and increasing rates of work hardening with increasing loading rate and grain size. Work hardening behavior is correlated with the substructural evolution of these specimens.     

亚波长光栅用于实现宽光谱消色散1/4波片的研究

基于严格耦合波理论 ,分析了共振区域矩形位相光栅的衍射特性 :位相延迟与光栅周期、占空比、槽深的关系 ,并设计出在 40 0～ 80 0nm范围内的消色散 1/4波片光栅 ,可以实现较为平坦的衍射效率和位相延迟曲线 ,其中位相延迟可保持在 90°左右 ,最大偏差小于 9% ,达到甚至优于普通二元复合消色散波片。通过对加工及安装误差的讨论 ,得到了影响消色散波片光栅性能的主要加工误差是槽深误差和占空比误差。     

Structure, properties, and thermal stability of nanocrystallite Fe-Ti-N soft magnetic films

We deposited Fe-Ti-N magnetic films with a high sputtering power of 7 W/cm/sup 2/. When the composition of the films was in the range of Fe-Ti(3.9 at.%)-N(8.8 at.%) to Fe-Ti(3.3 at.%)-N(13.5 at.%), the films were composed of /spl alpha/' and Ti/sub 2/N precipitates. With the addition of nitrogen, 4/spl pi/M/sub s/ became higher than that of pure iron, reaching a maximum of 23.8 kG. At the same time, H/sub c/ was reduced to a minimum of 1.12 Oe. The best films can meet the needs of the recording head in dual-element giant magnetoresistive/inductive heads, yielding high storage density (10 Gb/in/sup 2/). The incorporation of N in /spl alpha/-Fe brought about the /spl alpha/' phase with its higher saturation magnetization. Ti additions inhibited the equilibrium decomposition /spl alpha/'/spl rarr//spl alpha/+/spl gamma/'. Because H/sub C//sup D//spl prop/D/sup 6/, where D is average grain diameter, grain size control is very important. The nitrogen induces severe distortion of the /spl alpha/' lattice, which can cause the grains to break into pieces and reduce the grain size. High sputtering power also led to the formation of fine grains, with diameter in the order of 14 nm. Probably Ti/sub 2/N is preferentially precipitated on the grain boundary, pinning the grain boundary and stabilizing the grain size during high-temperature heat treatment. The temperature limit for stability of the structure and its associated low coercivity was not less than 520/spl deg/C.